Color card of product
Polyester Coating:
PE ACP which falls into matt and glossy series according to glossiness. The monomer of the backbone chain is the high molecular polymer of the ester bond, which is added with alkyd resin and ultraviolet absorbent. It is specially fit for interior decoration and advertising board. The structure of the polyester molecule is compact with a brilliant and rich surface which can fully satisfy the high demand for surface flatness in printing. The weather resistance is 8-10 years.
|
Raw Material |
Product Specifications |
||||||||
|
|
Product Data Sheet
| I.BOND(architecture) | I.BOND(advertising) | I.BOND(digital) | |||||||||||||
| Panel Thickness | Standard | Unit | 3mm | 4mm | 6mm | 2mm | 3mm | 4mm | 6mm | 2mm | 3mm | 4mm | 6mm | ||
| Thickness of Aluminium | DIN 1784 | mm | 0.5 | 0.5 | 0.5 | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | ||
| Aluminum thickness deviation | DIN 1784 | mm | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ±0.01 | ||
| Weight | Kg/m2 | 4.65 | 5.63 | 7.42 | 2.92 | 3.85 | 4.76 | 6.75 | 2.92 | 3.85 | 4.76 | 6.75 | |||
| Tolerance in length | DIN 16927 / ISO 11833-1 | mm | - 1 / +3 | - 01/ +3 | - 01/ +3 | - 0 / +2 | - 0 / +2 | - 0 / +2 | - 0 / +2 | - 0 / +2 | - 0 / +2 | - 0 / +2 | - 0 / +2 | ||
| Tolerance in width | DIN 16927 / ISO 11833-1 | mm | - 1 / +1.5 | - 1 / +1.5 | - 1 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | - 0 / +1.5 | ||
| Tolerance in thickness | DIN 16927 / ISO 11833-1 | mm | ± 0.15 | ± 0.15 | ± 0.15 | ± 0.15 | ± 0.10 | ± 0.10 | ± 0.15 | ± 0.15 | ± 0.10 | ± 0.10 | ± 0.15 | ||
| Horizontal flatness | DIN ISO 1101 | mm | 6 | 5 | 5 | 6 | 5 | 4 | 4 | 5 | 3 | 3 | 3 | ||
| Longitudinal roughness | DIN ISO 1101 | mm | 7 | 6 | 6 | 7 | 6 | 6 | 5 | 6 | 5 | 5 | 5 | ||
| Technical Properties | |||||||||||||||
| Section Modulus W | DIN 53293 | cm3/m | 1.25 | 1.75 | 2.75 | 1.01 | 1.25 | 1.75 | 2.75 | 1.32 | 1.55 | 1.85 | 2.96 | ||
| Rigidity (Poisson’s ratio μ = 0.3) E.I | DIN 53293 | kNm2/m | 0.14 | 0.28 | 0.63 | 0.67 | 0.14 | 0.28 | 0.63 | 0.97 | 0.16 | 0.34 | 0.86 | ||
| Alloy | EN 573-3 | ENAW | 1100 | 1100 | 3003 | ||||||||||
| Temper of Cover Sheets | EN 515 | H16/H18 | H16/H18 | H46/H42 | |||||||||||
| Modulus of Elasticity | EN 1999 1-1 | N/mm2 | 70,000 | 70,000 | 70,000 | ||||||||||
| Tensile Strength of Aluminium | EN 485-2 | N/mm2 | Rm ≥ 145 | Rm ≥ 145 | Rm ≥ 175 | ||||||||||
| 0.2% Proof Stress | EN 485-2 | N/mm2 | Rp0.2 ≥ 90 | Rp0.2 ≥ 90 | Rp0.2 ≥ 90 | ||||||||||
| Elongation | EN 485-2 | % | A50 ≥ 3 | A50 ≥ 3 | A50 ≥ 2 | ||||||||||
| Linear Thermal Expansion | EN 1999 1-1 | mm/m/℃ | 0.002 at 100℃ Temp difference | 0.020 at 100℃ Temp difference | 0.015 at 100℃ Temp difference | ||||||||||
| Core | |||||||||||||||
| Polyethylene, Typ LD-PE | g/cm3 | 0.935 | 0.935 | 0.935 | |||||||||||
| Surface | Coil Coating | Coil Coating | Coil Coating | ||||||||||||
| Lacquering | Fluorocarbon based (PVdF) | Fluorocarbon based (PE) | Fluorocarbon based (PE) | ||||||||||||
| Thickness of coating | µm | two coating：≥26，three coating:≥32 | ≥16 | ≥16 | ≥16 | ≥16 | ≥19 | ≥19 | ≥19 | ≥19 | |||||
| Gloss (initial value) | ECCA T2 | % | 30 - 80 | 20 - 100 | 20 - 100 | ||||||||||
| Pencil Hardness | ECCA T4 | H | 2H | 2H | |||||||||||
| Acoustical Properties | |||||||||||||||
| Sound Absorption Factor άs | ISO 354 | 0.05 | 0.05 | 0.05 | |||||||||||
| Sound Transmission Loss RW | ISO 717-1 | DB | 25 | 26 | 28 | 23 | 25 | 26 | 28 | 23 | 25 | 26 | 28 | ||
| Loss Factor d | EN ISO 6721 | 0.0072 | 0.0087 | 0.0138 | 0.0062 | 0.0072 | 0.0087 | 0.0138 | 0.0062 | 0.0072 | 0.0087 | 0.0138 | |||
| Thermal Properties | |||||||||||||||
| Thermal Resistance R | DIN 52612 | m2K/W | 0.0069 | 0.0103 | 0.0172 | 0.0036 | 0.0069 | 0.0103 | 0.0172 | 0.0036 | 0.0069 | 0.0103 | 0.0172 | ||
| Heat Transition Coefficient U | DIN 4108 | W/m2K | 5.65 | 5.54 | 5.34 | 5.98 | 5.65 | 5.54 | 5.34 | 5.98 | 5.65 | 5.54 | 5.34 | ||
| Temperature Range | ℃ | -50…+80 | -50…+80 | -50…+80 | |||||||||||